Adziski R.Fidancevska E.Anguseva B.Milosevski D.Vassilev V.Milosevski M.2024-07-102024-07-102024-07-102024-07-102008-12-010350-820X10.2298/SOS0801089ASCOPUS_ID:70849128532https://rlib.uctm.edu/handle/123456789/177Metallurgical slag with granulation (-0.125+0.063mm) and 20 wt% waste TV glass were used for obtaining a glass ceramic composite with a controlled porosity. This material obtained by sintering at 950°C/2h possessed thermal stability, integral porosity of 43.6% and E-modulus and bending strength of 12 GPa and 39 MPa, respectively. The composite was characterized with a permeability of 0.47 Da and generation of air bubbles with size of 1-4 mm in a water medium.enArticle