Ignatova K.Marcheva Y.2024-07-162024-07-162024-07-162024-07-162018-01-011314-79781314-7471SCOPUS_ID:85044741312https://rlib.uctm.edu/handle/123456789/1205The effect of NaH2PO2 concentration in the electrolyte (pH = 2) on the kinetics of NiP, CoP and NiCoP alloys electrodeposition at room temperature was studied. It was established that at concentration of NaH2PO2 about 0,2 M the deposition rate of NiP alloys decreases; the deposition rate of CoP alloys increases but at the same time the quality of the coating becomes bad. In both cases it was observed a depolarizing effect on the deposition. With increasing of the content of NaH2PO2, the phosphorus content in NiCoP alloys increases to approximately 7 % and the current efficiency of electrodeposition (CEE) goes over 100 %. The comparison of the kinetic data with those of CEE of NiCoP coatings showed that the mechanism of deposition is mixed chemical-electrochemical.enArticle