Browsing by Author "Nenov T."

Now showing 1 - 3 of 3
  • No Thumbnail Available
    Item
    Elucidation of the contribution of modified titania films over the performance of thin film humidity sensors
    (2013-05-21) Kozhukharov S.; Nenova Z.; Nenov T.; Ivanov S.; Machkova M.
    The present research focuses on comparative measurements of the influence of complex additives on the sensitivity of humidity sensors, prepared by the sol-gel metrhod. Three different dopants were added to the primary mixture in order to improve the properties of the films, expressed in water uptake capability, as follows: Bismuth acetate (CH3COO)3Bi, Vanadium-2,4 pentadionate (C15H21O6V), and Sodium tert-butoxide (CH3)3CONa. The properties of the obtained sensors were evaluated by determination of their electrical resistances in a chamber with controlled humidity. As a result, it was experimentally established that the most significant positive effect over both the increase of sensitivity and the measurement range enlargement come from V(III)-2,4 pentadionate with Sodium tert-butoxide.
  • No Thumbnail Available
    Item
    Humidity Sensing Elements Based on Silica-Graphene Surface Layers
    (2024-01-01) Nedev N.; Nenova Z.; Kozhukharov S.; Ivanov S.; Nenov T.
    The paper presents humidity sensing elements based on silica-graphene surface layers, prepared via a sol-gel method. The samples were sintered at temperatures of 400 °C, 600 °C and 800 °C. Tetraethoxysilane was used as a precursor of SiO2 and as a dopant - graphene aggregates of nanoplatelets. A description of the sample preparation procedure is provided. Using a precise impedance analyzer and a calibrator for humidity and temperature, the changes in their resistance R were investigated with variations in relative humidity in the range of 30% to 90% at a temperature of 25 °C and at a frequency of 20 Hz. Morphological observations and map data analyses were carried out by Scanning Electron Microscopy (SEM) and Energy Dispersion Spectroscopy (EDX). The developed sensor elements have a good sensitivity to the humidity, and the resistance change reaches two orders of magnitude. Additions of graphene improve the sensitivity of the elements. The characteristics of the sensing elements at different sintering temperatures and different amounts of graphene dopant were modeled using an artificial neural network.
  • No Thumbnail Available
    Item
    Influence of ce(iii)/ce(iv)-supplements on the characteristics of humidity sensors with tio2 films prepared via a sol-gel method
    (2013-03-01) Kozhukharov S.; Nenova Z.; Nenov T.; Machkova M.; Kozhukharov V.
    Humidity sensors have been prepared via a sol-gel method to deposit TiO2 films with additions of Ce-compounds on alumina substrates, with interdigitated silver palladium electrodes. Observations by scanning electron microscopy (SEM) were performed in order to determine the surface morphology of the respective layers. Structural and compositional characterization was done by X-ray diffraction analysis (XRD), and energy dispersive X-ray spectroscopy (EDX) for investigation of the relation between the film structures and the parameters of the respective sensors. The influence of Ce-compounds on the electrical characteristics of the samples as humidity sensing elements has been evaluated by an impedance analyzer.